Wax Rolls
WR-200 YELLOW
Structure
Very Coarse Crystaline
Melting Point
60-62’C
Penetration (25’C)
10-11
Avg. Coating on 30’s Cotton yarn
Medium
Applications
Particularly for Medium and fine counts yarn (cotton / synthetics), with extreme ambient temperature (near 85F)
| Wax Rolls | Colorcode | Structure | MeltingPoint | Penetration | Avg wax pick up on 30' Count | Application |
|---|---|---|---|---|---|---|
|
WR-100 GREEN
|
 |
Coarse Crystaline
|
59-61’C
|
19-20
|
Low(0.04 to 0.06%)
|
Universal grade for cotton, wool, rayon, acrylic, blends, etc.
|
|
WR-200 YELLOW
|
 |
Very Coarse Crystaline
|
60-62’C
|
10-11
|
Medium(0.08 to 0.1%)
|
Particularly for Medium and fine counts yarn (cotton / synthetics), with extreme ambient temperature (near 85F)
|
|
WR-300 BLUE
|
 |
Very Coarse Crystaline
|
56-58’C
|
24-25
|
High(0.1 to 0.12%)
|
For soft twist and bleached yarns at low winding tension & High speed sewing threads.
|
|
WR-400 PINK
|
 |
Coarse Crystaline
|
59-61’C
|
19-20
|
Low(0.05 to 0.07%)
|
Water soluble, for fabrics to be dyed or bleached.
|
|
WR-500 VIOLET
|
|
Very Coarse Crystaline
|
60-62’C
|
10-11
|
Medium(0.08 to 0.1%)
|
Water soluble, for fabrics to be dyed or bleached for ambient temp above / 75’F
|
|
SL-40 (WHITE) SUPERIOR
|
 |
Very-Fine Crystalline
|
59-60’C
|
18-20
|
High(0.12 to 0.15%)
|
Suitable for high speed sewing threads superior shine & lustrous finish to yarn.
|
|
SL-30 (WHITE)
SUPERIOR LUBRICATION
|
|
fine Crystaline
|
59-60’C
|
16-18
|
High(0.15 to 0.02%)
|
Universal grade for cotton, polyster, blends, melange yarn, etc.
|
|
SL20 (WHITE) SILICONE WAX
|
|
Very-Fine Crystalline
|
59-60’C
|
16-18
|
Very High(0.20 to 0.25%)
|
Universal grade for cotton, polyster, blends, melange yarn, etc.
|
|
SL-10 (ORANGE) SILICONE WAX
|
 |
Super fine Crystaline
|
58-60’C
|
16-18
|
Very High(0.25 to 0.03%)
|
Suitable for high speed sewing threads superior shine & lustrous finish to yarn.
|
|
WR-3000 (WHITE)
|
|
Fine Crystaline
|
75-80’C
|
8-9
|
Medium(0.1 to 0.12%)
|
For medium & fine counts yarn cotton / polyster hosiery yam,suitable for yarn to be condition at very high temp. (above 75 deg o).
|
|
WR-112 (WHITE) BLENDED WAX
|
|
Coarse Crystaline
|
62-64’C
|
10-12
|
Medium (0.08 to 0.1%)
|
For medium & fine counts yarn cotton / polyster hosiery yarn.
|
CHEMAX WAX ROLLS SIZE OFFERED
Outer Box Dimension : 17 Inch L X 14.5 Inch B x 10.5 Inch H. Gross Wt.: 16 Kgs| Sr. No. | Size | MACHINE | HOLE TYPE |
|---|---|---|---|
|
1
|
2'OD X 80 CMS LENGTH
|
WAX BAR - LOOMS
|
TRANGLE
|
|
2
|
2'X X 2' X 2' X 18 Inch Length
|
WAX TRIANGLES - LOOMS
|
CIRCULAR
|
|
3
|
38MMOD X 15.2MM ID X 15MM HT
|
CONE WINDERS
|
CIRCULAR
|
|
4
|
38MM OD X 13 MM ID X 20MM HT
|
MURATA JET SPG (MJS)
|
CIRCULAR
|
|
5
|
38MM OD X 15.2MM ID X 20MM HT
|
CONE WINDERS
|
CIRCULAR
|
|
6
|
38MM OD X15.2MM ID X 26MM HT
|
CONE WINDERS
|
CIRCULAR
|
|
7
|
38MM OD X 13 MM ID X 32MM HT
|
MURATA AUTOCONER
|
CIRCULAR
|
|
8
|
38MM OD X 13 MM ID X 45MM HT
|
MURATA (21C MODEL)
|
CIRCULAR
|
|
9
|
38MMOD X 13.5MM ID X 45MM HT
|
SCHLAFHORST / SAVIO
|
Sq BOTTOM
|
|
10
|
38MM OD X 15.2MM ID X 45MM HT.
|
SCHLAFHORST / SAVIO
|
CIRCULAR
|
|
11
|
40MM OD X 13.5MM ID X 15MM HT
|
SSM WINDERS
|
SQUARE
|
|
12
|
40MM OD X 13.5MM ID X 45MM HT
|
SSM WINDERS
|
SQUARE
|
|
13
|
45MM OD X 12.5MM ID X 15MM HT
|
SSM WINDERS
|
CIRCULAR
|
|
14
|
45MM OD X 12.5MM ID X 20MM HT
|
SSM WINDERS
|
SQUARE
|
|
15
|
45MM OD X 12.5MM ID X 25MM HT
|
MVS WINDERS
|
SQUARE
|
|
16
|
45MM OD X 12.5MM ID X 45MM HT
|
REITER
|
SQUARE
|
|
17
|
45MM OD X 14MM ID X 15MM HT
|
SSM WINDERS
|
SQUARE
|
|
18
|
45MM OD X 15.4MM ID X 15MM HT
|
SSM WINDERS
|
CIRCULAR
|
|
19
|
45MM OD X14MM ID X 25MM HT
|
SSM WINDERS
|
SQUARE
|
|
20
|
45MM OD X 14MM ID X 45MM HT
|
SSM WINDERS
|
SQUARE
|
|
21
|
45MM OD X 15.4MM ID X 12MM HT
|
SSM WINDERS
|
CIRCULAR
|
|
22
|
45MM OD X 15.4MM ID X 20MM HT
|
SSM WINDERS
|
CIRCULAR
|
|
23
|
45MM OD X 15.4MM ID X 25MM HT
|
SSM WINDERS
|
CIRCULAR
|
|
25
|
60mmOD X15MM /13.5MM ID X 41 MMHT
|
Schlafhorst OE
|
Sq BOTTOM
|
|
26
|
75MM OD X 21MM ID X 45MM HT
|
OE RIETER
|
SQUARE
|
Reviews
There are no reviews yet.